低磁钢在长期使用过程中会出现腐蚀破坏,影响使用寿命。以环氧树脂601作为成膜树脂,通过试验选出合适的活性稀释剂和固化剂,同时添加适当的颜填料,制备出一种可在低磁钢表面应用的高固体分环氧防腐蚀涂料,该种涂料在低磁钢表面具有优异的附着力、耐冲击性和耐介质性能,施工性能良好,可以满足低磁钢在不同环境下的防腐要求。
Low magnetic steel will have corrosion damage in the long-term use process,which will affect the service life.The epoxy resin 601 was used as film-forming resin,and the appropriate active diluent and curing agent were selected through experiments.At the same time,appropriate pigments and fillers were added to prepare a kind of high solid epoxy anti-corrosion coating which can be applied on the surface of low magnetic steel.The coating had excellent adhesion,impact resistance and medium resistance,and good construction performance on the surface of low magnetic steel.It can meet the anti-corrosion requirements of low magnetic steel in different environments.
[1] 周鑫磊,王世安,王大伟.舰艇用低磁钢的开发及应用[J].材料开发与应用,2012(2):84-88.
[2] 张建民.海洋性气候环境下低磁钢板防腐工艺研究[J].涂料工业,2020,50(9):24-27.
[3] 康瑞瑞.无溶剂重防腐环氧涂料的制备与研究[J].涂料工业,2021,51(2):54-60.
[4] 李伟华,田惠文,宗成中,等.低表面处理涂料的配方设计和研究进展[J].涂料工业,2008,38(2):50-54.
[5] 郝朋,闫林森,东继莲.环氧粉末涂层对金属基材附着力的影响因素[J].涂料工业,2020,50(4):26-30.
[6] 柴红梅,孙超明,李鹏,等.活性稀释剂含量对E-51环氧树脂体系性能的影响[J].材料工程,2008,20(6):285-286.
[7] Varley R J.Toughening of epoxy resin systems using low viscosity additives[J].Polymer International,2004,53(1):78-84.
[8] 靳昊,姚嘉,易忠来.活性稀释剂对环氧树脂快速修复材料性能的影响[J].铁道建筑,2020,60(9):156-158.
[9] 孙曼灵.环氧树脂应用原理与技术[M].北京:机械工业出版社,2002,253-256.
[10] 方倩,郭常青,张善贵,等.新型带锈带湿带油涂装涂料的研制[J].涂料工业,2014,44(2):1-6.
[11] 宋世红.工业用改性环氧低表面处理底漆的研制[J].中国涂料,2008,23(4):47-51.
PDF